Products Introduction: SuperSplice
Type: SS35, SS63, SS80, SS85, SS105,SS125,SS250
Framework:Nylon fiber
Nylon fiber are used to manufacture rubber conveyor belt. It have high tensile strength, high impact resistant, high tear resistance.
Our SuperSplice is made with Nylon fabric as its framework material. We use a new textile process to make the warp tension and weft tension of nylon fabric the same and have high strength.
Nylon performance Table:
| No. | Items | Unit | Test Result | Reference: 1 ply fabric thickness without rubber: Type EP100 (thickness 0.5mm) |
| 1 | 1 ply fabric thickness | mm | 1.7 | EP100(0.5),EP150(0.7),EP200(0.8), EP300(1.25),EP400(1.35) |
| 2 | Warp Breaking Strength | N/ mm | 300 | |
| 3 | Weft Breaking Strength | N/ mm | 300 |
SuperSplice product series:
| No. | Type | Width (mm) |
Top plate | Bottom plate | Screws quantity/m (units) |
||||
| Nylon plies (P) |
Whole tensile strength (N/ mm) |
Thickness (mm) |
Nylon plies (P) |
Whole tensile strength (N/ mm) |
Thickness (mm) |
||||
| 1 | SS35 | 65 | 1 | 300 | 3.5 | 1 | 300 | 3.5 | ∅5:96 |
| 2 | SS63 | 110 | 2 | 600 | 5~5.5 | 2 | 600 | 4.5~5.5 | ∅5:191 |
| 3 | SS80 | 156 | 2 | 600 | 5.5~6.5 | 2 | 600 | 4.5~5.5 | ∅5:286 |
| 5 | SS125 | 260 | 3 | 900 | 6.5~7.5 | 2 | 600 | 4.5~5.5 | ∅6:286 |
| 6 | SS250 | 260 | 4 | 1200 | 7.5~8.5 | 3 | 900 | 6.5~7.5 | ∅6:286 |
Rubber grade
| No. | Rubber grade | ||
| 1 | Abrasion resistant | Tensile strength: 25MPA | Abrasion less 60mm3 |
| 2 | Heat resistant | Heat resistant 300℃ | |
| 3 | Oil resistant | Tensile strength: 20MPA | Abrasion less 150mm3 |
| 4 | acid and alkali resistant |
Tensile strength: 20MPA | Abrasion less 150mm3 |
Products Introduction: SuperSplice
Type:SS35K,SS63K,SS80K,SS85K,SS105K,SS125K,SS250K
K:indicates Kevlar fiber.
Kevlar fiber are used to manufacture bulletproof helmets and bulletproof vests. It strength is five times that of steel. It can withstand temperatures up to 600℃.
Our SuperSplice is made with Kevlar fabric as its framework material. It has super high tensile strength, super high impact resistance, super high wear resistance and heat resistance.
Kevlar performance Table:
Kevlar performance Table:
| No. | Items | Unit | Test Result |
| 1 | 1 ply fabric thickness | mm | 1.2 |
| 2 | Warp Breaking Strength | N/ mm | 500 |
| 3 | Weft Breaking Strength | N/ mm | 260 |
| 4 | Elongation at Break Warp | % | 2.7 |
| 5 | Elongation at Break Weft | % | 0.6 |
SuperSplice product series:
| No. | Type | Width (mm) |
Top plate | Bottom plate | Screws quantity/m (units) |
||||
| Kevlar plies (P) |
Whole tensile strength (N/ mm) |
Thickness (mm) |
Kevlar plies(P) |
Whole tensile strength (N/ mm) |
Thickness (mm) |
||||
| 1 | SS35K | 65 | 1 | 500 | 3.5 | 1 | 500 | 3.5 | ø5:96 |
| 2 | SS63K | 110 | 2 | 1000 | 5~5.5 | 2 | 1000 | 4.5~5.5 | ø5:191 |
| 3 | SS80K | 156 | 3 | 1500 | 5.5~6.5 | 2 | 1000 | 4.5~5.5 | ∅5:286 |
| 4 | SS105K | 156 | 3 | 1500 | 5.5~6.5 | 2 | 1000 | 4.5~5.5 | ∅5:286 |
| 5 | SS125K | 260 | 3 | 1500 | 5.5~6.5 | 2 | 1000 | 4.5~5.5 | ∅6:286 |
| 6 | SS250K | 500 | 4 | 2000 | 6.5~7.5 | 3 | 1500 | 5.5~6.5 | ∅6:286 |
Rubber grade
| No. | Rubber grade | ||
| 1 | Abrasion resistant | Tensile strength: 25MPA | Abrasion less 60mm3 |
| 2 | Heat resistant | Heat resistant 300°C | |